Name: ESRA-CYC-0005: Galvanostatic Cycling (charge–discharge) of Cell 2025_BingningWang_ChenLiao_Nat.Commun._s41467-025-57961-w
Creator: Bingning Wang
Published: 2026-08-13
License: https://spdx.org/licenses/CC-BY-4.0

Researcher

Bingning Wang

ORCID

0000-0001-5168-6493

PI(s)

Chen Liao

Project

Data-driven design of electrolyte additives for 5 V LNMO electrodes

Sample ID

2025_BingningWang_ChenLiao_Nat.Commun._s41467-025-57961-w ← click to see all uploads with this sample ID

Publication DOI

10.1038/s41467-025-57961-w ↗

External Data URL

https://github.com/hieuadoan/ML-LNMO-additives ↗

Upload Date (CDT)

2026-08-13 10:19:26

Upload ID

ab09581e-730b-48cc-af71-d044320335ab

How to Cite

1 — Cite the dataset paper

↗ View paper

2 — Cite the ESRA platform

Galib, M. et al. (2026). ESRA: Energy Storage Research Assistant. Argonne National Laboratory. https://github.com/MusannaGalib/esra-platform

CC BY 4.0 · Data shared under Creative Commons Attribution 4.0

You must log in to edit this record.

PI Name(s)

Project

Sample ID

Publication DOI

Notes

Cycling fields

Fill any blank required field to clear the Incomplete flag.

Cell Type

Cathode Material *

Anode Material *

Cell Geometry *

Cell Geometry Verbatim

Electrode Area Cm2 *

Active Mass Cathode Mg

Active Mass Anode Mg

Specific Capacity Mah G

Theoretical Capacity Mah

Temperature C

Electrolyte

Voltage Window Lower V

Voltage Window Upper V

Stack Pressure Mpa

Protocol Summary

Number Of Cycles

Materials studied

Shared by all 6 datasets on 2025_BingningWang_ChenLiao_Nat.Commun._s41467-025-57961-w. Edits apply to every one.

No materials declared yet.

or press Ctrl S

Researcher name, ORCID and experiment type cannot be changed after upload.

Storage LocationNERSC Community File System

Path

/global/cfs/cdirs/m4845/gsharing/bingning-wang/data-driven-design-of-electrolyte-additi/2025-bingningwang-chenliao-natcommun-s41/BATTERY_CYCLING/cycling/ESRA-CYC-0005/

Open in Globus File Manager →

Linked Uploads

Other datasets with the same sample ID (2025_BingningWang_ChenLiao_Nat.Commun._s41467-025-57961-w).

Type	Group	Date	Project	Link
SEM	Chen Liao	2026-08-13 10:19	Data-driven design of electrolyte additives for 5 V LNMO electrodes	same sample
XPS	Chen Liao	2026-08-13 10:19	Data-driven design of electrolyte additives for 5 V LNMO electrodes	same sample
NMR	Chen Liao	2026-08-13 10:19	Data-driven design of electrolyte additives for 5 V LNMO electrodes	same sample
MLIP	Chen Liao	2026-08-13 10:19	Data-driven design of electrolyte additives for 5 V LNMO electrodes	same sample
EIS	Chen Liao	2026-08-13 10:19	Data-driven design of electrolyte additives for 5 V LNMO electrodes	same sample

Materials Studied 6 materials

Material	Family	Role(s)	Ion
LiNi0.5Mn1.5O4 (LNMO) · High-voltage spinel cathode 5 V-class spinel Purchased / commercial Argonne Cell Analysis, Modeling and Prototyping (CAMP) facility Electrode fabrication Slot die coat — Laminate coated by Argonne CAMP facility in a dry room equipment: automatic slot die coateratmosphere: dry room Methods, Positive/negative electrodes Vacuum dry temperature: 80 °C Methods, Positive/negative electrodes Vacuum dry — Dried again immediately before use atmosphere: Ar-filled gloveboxtemperature: 100 °C Methods, Positive/negative electrodes	Spinel Cathode	Cathode	Li
Graphite · Graphite anode Purchased / commercial Argonne Cell Analysis, Modeling and Prototyping (CAMP) facility Electrode fabrication Slot die coat — Laminate coated by Argonne CAMP facility in a dry room equipment: automatic slot die coateratmosphere: dry room Methods, Positive/negative electrodes Vacuum dry temperature: 80 °C Methods, Positive/negative electrodes Vacuum dry — Dried again immediately before use atmosphere: Ar-filled gloveboxtemperature: 100 °C Methods, Positive/negative electrodes	Graphite Anode	Anode	Li
1.0 M LiPF6 in EC/EMC · Baseline carbonate electrolyte Purchased / commercial	Carbonate Liquid	Electrolyte, Solvent	Li
LiPF6 · Lithium hexafluorophosphate Purchased / commercial	Lithium salt Other · as named	Salt	Li
Electrolyte additive library (28 additives + ML-designed binary blends) · Screened electrolyte additives Machine-learning-guided additive and binary-blend screening Purchased / commercial Electrolyte preparation Add — Dose additive into the baseline electrolyte solvent: 1.0 M LiPF6 in EC/EMC 1/9composition ratio: 0.25-10 wt% of the total formulation (e.g. 0.25 wt% tVCBO + 1 wt% MS) Methods; additive table	Electrolyte additive set Other · as named	Additive	Li
Celgard polyolefin separator · Celgard separator Purchased / commercial Celgard Sample preparation Dry duration: overnighttemperature: 50 °C Methods, coin cells	Separator material Other	Separator	—

Declared for sample 2025_BingningWang_ChenLiao_Nat.Commun._s41467-025-57961-w — shared by every dataset on this sample.

Experiment Metadata

Visibility	public
Electrolyte	1.0 M LiPF6 in EC/EMC (1:9 v/v) + additive(s)
Anode Material	Graphite (Superior Graphite SLC1506T)
Publication Doi	10.1038/s41467-025-57961-w
Number Of Cycles	100 (4 loops × RPT/aging + final RPT ≈ 100 cycles)
Cathode Material	LiNi0.5Mn1.5O4 (LNMO, Targray 5V spinel)
Institution Code	ESRA
Voltage Window — Lower	3.8
Voltage Window — Upper	4.7
Theoretical Capacity Mah	120.0
Current / C-Rate / Protocol Summary	Formation: 5 cycles at C/10; RPT: C/25; Aging: C/3 with 1 h CV hold at 4.7 V (to C/20); 4 loops total; final RPT at C/25; HPPC pulses at 2C discharge / 1.5C charge

Uploaded Files 165 files · 2.0 GB